Corrosion of NiCoCrAIY Coatings and TBC Systems Subjected to Water Vapor and Sodium Sulfate
Siemens AG, Energy Sector, Berlin, Germany.
Linköpings universitet, Institutionen för ekonomisk och industriell utveckling. Linköpings universitet, Tekniska fakulteten.
Siemens Industrial Turbomachinery AB, Finspång, Sweden.
Linköpings universitet, Institutionen för ekonomisk och industriell utveckling, Konstruktionsmaterial. Linköpings universitet, Tekniska fakulteten.
2015 (Engelska)Ingår i: Journal of thermal spray technology (Print), ISSN 1059-9630, E-ISSN 1544-1016, Vol. 24, nr 6, 953-964 s.Artikel i tidskrift (Refereegranskat) Published
Abstract [en]

Thermal barrier coating (TBC) systems are commonly used in gas turbines for protection against high-temperature degradation. Penetration of the ceramic top coat by corrosive species may cause corrosion damage on the underlying NiCoCrAlY bond coat and cause failure of the TBC system. In the current study, four oxidation/corrosion conditions were tried: (i) lab air, (ii) water vapor, (iii) sodium sulfate deposited on the specimens, and (iv) water vapor + sodium sulfate. The test was done at 750 °C in a cyclic test rig with 48 h cycles. The corrosion damage was studied on NiCoCrAlY-coated specimens, thin APS TBC specimens, and thick APS TBC specimens. Water vapor was found to have very minor influence on the oxidation, while sodium sulfate increased the TGO thickness both for NiCoCrAlY specimens and TBC-coated specimens; the influence of the TBC thickness was found to be very small. Sodium sulfate promoted thicker TGO; more Cr-rich TGO; the formation of Y oxides, and internally, Y sulfides; pore formation in the coating as well as in the substrate; and the formation of a Cr-depleted zone in the substrate.

Ort, förlag, år, upplaga, sidor
Springer, 2015. Vol. 24, nr 6, 953-964 s.
Nyckelord [en]
corrosion, cyclic furnace, sodium sulfate, thermal barrier coating, water vapor
Nationell ämneskategori
Korrosionsteknik
Identifikatorer
URN: urn:nbn:se:liu:diva-119690DOI: 10.1007/s11666-015-0253-zISI: 000358965400007OAI: oai:DiVA.org:liu-119690DiVA: diva2:825917
Tillgänglig från: 2015-06-24 Skapad: 2015-06-24 Senast uppdaterad: 2015-08-28

Open Access i DiVA

Fulltext saknas

Övriga länkar

Förlagets fulltext

Sök vidare i DiVA

Av författaren/redaktören
Eriksson, RobertYuan, KangPeng, Ru
Av organisationen
Institutionen för ekonomisk och industriell utvecklingTekniska fakultetenKonstruktionsmaterial
I samma tidskrift
Journal of thermal spray technology (Print)
Korrosionsteknik

Sök vidare utanför DiVA

GoogleGoogle Scholar

Altmetricpoäng

Totalt: 99 träffar
RefereraExporteraLänk till posten
Permanent länk

Direktlänk
Referera
Referensformat
  • apa
  • harvard1
  • ieee
  • modern-language-association-8th-edition
  • vancouver
  • oxford
  • Annat format
Fler format
Språk
  • de-DE
  • en-GB
  • en-US
  • fi-FI
  • nn-NO
  • nn-NB
  • sv-SE
  • Annat språk
Fler språk
Utmatningsformat
  • html
  • text
  • asciidoc
  • rtf