TiBx thin films grown from compound TiB2 targets by magnetron sputter deposition are typically highly over-stoichiometric, with x ranging from 3.5 to 2.4, due to differences in Ti and B preferential-ejection angles and gas-phase scattering during transport from the target to the substrate. Here, the authors demonstrate that stoichiometric TiB2 films can be obtained using highpower impulse magnetron sputtering (HiPIMS) operated in power-controlled mode. The B/Ti ratio x of films sputter-deposited in Ar is controllably varied from 2.08 to 1.83 by adjusting the length of HiPIMS pulses t(on) between 100 and 30 mu s, while maintaining average power and pulse frequency constant. This results in peak current densities J(T), peak ranging from 0.27 to 0.88 A/cm(2). Energy- and time-resolved mass spectrometry analyses of the ion fluxes incident at the substrate position show that the density of metal ions increases with decreasing t(on) due to a dramatic increase in J(T, peak) resulting in the strong gas rarefaction. With t(on)amp;lt;60 mu s (J(T),(peak)amp;gt; 0.4 A/cm(2)), film growth is increasingly controlled by ions incident at the substrate, rather than neutrals, as a result of the higher plasma dencity and, hence, electron-impact ionization probablity. Thus, since sputter- ejected Ti atoms have a higher probability of being ionized than B atoms, due to their lower first-ionization potential and larger ionization cross-section, the Ti concentration in as-deposited films increases with decreasing ton (increasing J(T,peak)) as ionized sputtered species are steered to the substrate by the plasma in order to maintain charge neutrality. Published by the AVS.

Refractory transition-metal diborides exhibit inherent hardness. However, this is not always sufficient to prevent failure in applications involving high mechanical and thermal stress, since hardness is typically accompanied by brittleness leading to crack formation and propagation. Toughness, the combination of hardness and ductility, is required to avoid brittle fracture. Here, the authors demonstrate a strategy for simultaneously enhancing both hardness and ductility of ZrB2-rich thin films grown in pure Ar on Al2O3(0001) and Si(001) substrates at 475 degrees C. ZrB2.4 layers are deposited by dc magnetron sputtering (DCMS) from a ZrB2 target, while Zr1-xTaxBy alloy films are grown, thus varying the B/metal ratio as a function of x, by adding pulsed high-power impulse magnetron sputtering (HiPIMS) from a Ta target to deposit Zr1-xTaxBy alloy films using hybrid Ta-HiPIMS/ZrB2-DCMS sputtering with a substrate bias synchronized to the metal-rich portion of each HiPIMS pulse. The average power P-Ta (and pulse frequency) applied to the HiPIMS Ta target is varied from 0 to 1800W (0 to 300 Hz) in increments of 600W (100 Hz). The resulting boron-to-metal ratio, y = B/(Zr+Ta), in as-deposited Zr1-xTaxBy films decreases from 2.4 to 1.5 as P-Ta is increased from 0 to 1800W, while x increases from 0 to 0.3. A combination of x-ray diffraction (XRD), glancing-angle XRD, transmission electron microscopy (TEM), analytical Z-contrast scanning TEM, electron energy-loss spectroscopy, energy-dispersive x-ray spectroscopy, x-ray photoelectron spectroscopy, and atom-probe tomography reveals that all films have the hexagonal AlB2 crystal structure with a columnar nanostructure, in which the column boundaries of layers with 0 amp;lt;= x amp;lt; 0.2 are B-rich, whereas those with x amp;gt;= 0.2 are Ta-rich. The nanostructural transition, combined with changes in average column widths, results in an similar to 20% increase in hardness, from 35 to 42 GPa, with a simultaneous increase of similar to 30% in nanoindentation toughness, from 4.0 to 5.2MPa root m. Published by the AVS.

We recently showed that Zr1−xTaxBy thin films have columnar nanostructure in which column boundaries are B-rich for x < 0.2, while Ta-rich for x ≥ 0.2. Layers with x ≥ 0.2 exhibit higher hardness and, simultaneously, enhanced toughness. Here, we determine the atomic-scale nanostructure of sputter-deposited columnar Zr0.7Ta0.3B1.5 thin films. The columns, 95 ± 17 Å, are core/shell nanostructures in which 80 ± 15-Å cores are crystalline hexagonal-AlB2-structure Zr-rich stoichiometric Zr1−xTaxB2. The shell structure is a narrow dense, disordered region that is Ta-rich and highly B-deficient. The cores are formed under intense ion mixing via preferential Ta segregation, due to the lower formation enthalpy of TaB2 than ZrB2, in response to the chemical driving force to form a stoichiometric compound. The films with unique combination of nanosized crystalline cores and dense metallic-glass-like shells provide excellent mechanical properties.

We recently showed that sputter-deposited Zr_1-xTa_xB_y thin films have hexagonal AlB₂-type columnar nanostructure in which column boundaries are B-rich for x < 0.2, while Ta-rich for x ≥ 0.2. As-deposited layers with x ≥ 0.2 exhibit higher hardness and, simultaneously, enhanced toughness. Here, we study the mechanical properties of ZrB_2.4, Zr_0.8Ta_0.2B_1.8, and Zr_0.7Ta_0.3B_1.5 films annealed in Ar atmosphere as a function of annealing temperature T_a up to 1200 °C. In-situ and ex-situ nanoindentation analyses reveal that all films undergo age hardening up to T_a = 800 °C, with the highest hardness achieved for Zr_0.8Ta_0.2B_1.8 (45.5±1.0 GPa). The age hardening, which occurs without any phase separation or decomposition, can be explained by point-defect recovery that enhances chemical bond density. Although hardness decreases at T_a > 800 °C due mainly to recrystallization, column coarsening, and planar defect annihilation, all layers show hardness values above 34 GPa over the entire T_a range.

Refractory transition-metal diborides (TMB2) are candidates for extreme environments due to melting points above 3000 degrees C, excellent hardness, good chemical stability, and thermal and electrical conductivity. However, they typically suffer from rapid high-temperature oxidation. Here, we study the effect of Al addition on the oxidation properties of sputter-deposited TiB2-rich Ti1-xAlxBy thin films and demonstrate that alloying the films with Al significantly increases the oxidation resistance with a slight decrease in hardness. TiB2.4 layers are deposited by dc magnetron sputtering (DCMS) from a TiB2 target, while Ti1-xAlxBy alloy films are grown by hybrid high-power impulse and dc magnetron co-sputtering (Al-HiPIMS/TiB2-DCMS). All as-deposited films exhibit columnar structure. The column boundaries of TiB2.4 are B-rich, while Ti0.68Al0.32B1.35 alloys have Ti-rich columns surrounded by a Ti(1-x)Al(x)By tissue phase which is predominantly Al rich. Air-annealing TiB2.4 at temperatures above 500 degrees C leads to the formation of oxide scales that do not contain B and mostly consist of a rutile-TiO2 (s) phase. The resulting oxidation products are highly porous due to the evaporation of B2O3 (g) phase as well as the coarsening of TiO2 crystallites. This poor oxidation resistance is significantly improved by alloying with Al. While air-annealing at 800 degrees C for 0.5 h results in the formation of an similar to 1900-nm oxide scale on TiB2.4, the thickness of the scale formed on the Ti0.68Al0.32B1.35 alloys is similar to 470 nm. The enhanced oxidation resistance is attributed to the formation of a dense, protective Al-containing oxide scale that considerably decreases the oxygen diffusion rate by suppressing the oxide-crystallites coarsening. (C) 2020 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Refractory transition-metal (TM) diborides have high melting points, excellent hardness, and good  chemical  stability.  However, these properties are not sufficient for applications involving extreme  environments that require high mechanical strength as well as oxidation and corrosion resistance. Here, we study the effect of Cr addition on the properties of ZrB₂-rich Zr₁-_xCr_xB_y thin films grown by hybrid high-power impulse and dc magnetron co-sputtering (Cr-HiPIMS/ZrB₂-DCMS) with a 100-V Cr-metal-ion synchronized potential. Cr metal fraction, x = Cr/(Zr+Cr), is increased from 0.23 to 0.44 by decreasing the power P_zrb2 applied to the DCMS ZrB₂ target from 4000 to 2000 W, while the average power, pulse width, and frequency applied to the HiPIMS Cr target are maintained constant. In addition, y decreases from 2.18 to 1.11 as a function of P_zrb2, as a result of supplying Cr to the growing film and preferential B resputtering caused by the pulsed Cr-ion flux. ZrB_2.18, Zr_0.77Cr_0.23B_1.52, Zr_0.71Cr_0.29B_1.42, and Zr_0.68Cr_0.32B_1.38 2 films have hexagonal AlB₂ crystal structure with a columnar nanostructure, while Zr_0.64Cr_0.36B_1.30 and Zr_0.56Cr_0.44B_1.11 are  amorphous. All films show hardness above 30 GPa. Zr_0.56Cr_0.44B_1.11 alloys exhibit much better toughness, wear, oxidation, and corrosion resistance than ZrB_2.18. This combination of properties   makes Zr_0.56Cr_0.44B_1.11 ideal candidates for numerous strategic applications.

There is a need for developing synthesis techniques that allow the growth of high-quality functional films at low substrate temperatures to minimize energy consumption and enable coating temperature-sensitive substrates. A typical shortcoming of conventional low-temperature growth strategies is insufficient atomic mobility, which leads to porous microstructures with impurity incorporation due to atmosphere exposure, and, in turn, poor mechanical properties. Here, we report the synthesis of dense Ti_0.67Hf_0.33B_1.7 thin films with a hardness of ∼41.0 GPa grown without external heating (substrate temperature below ∼100 °C) by hybrid high-power impulse and dc magnetron co-sputtering (HfB₂-HiPIMS/TiB₂-DCMS) in pure Ar on Al₂O₃(0001) substrates. A substrate bias potential of −300 V is synchronized to the target-ion-rich portion of each HiPIMS pulse. The limited atomic mobility inherent to such desired low-temperature deposition is compensated for by heavy-mass ion (Hf⁺) irradiation promoting the growth of dense Ti_0.67Hf_0.33B_1.7.