Alternative method for deposition of alumina thin films
Linköping University, Department of Physics, Chemistry and Biology.
2009 (English)Independent thesis Advanced level (degree of Master (Two Years)), 20 credits / 30 HE creditsStudent thesis
Abstract [en]

Deposition of alumina thin films in the presence of fluorine as a method for reducing thehydrogen incorporation in the films was investigated in this thesis. Hydrogen incorporated in alumina thin films have been shown to cause a lower density and refractive index in amorphous films, assist electrical conduction through thin amorphous films as well as inhibiting the formation of the thermally stable α-phase.

The depositions were made in a ultra high vacuum system where high vacuum conditions were simulated by leaking water vapor into the system. No substrate heating or substratebias was applied. Films were deposited at a range of fluorine partial pressures, from 2,5×10-6- 5×10-5 Torr, and were analyzed by elastic recoil detection analysis, nuclear reaction analysis, scanning electron microscopy and x-ray diffraction. Mass spectrometry measurements were done during the depositions to analyze the deposition process.

The mass spectrometry investigations show that there is a trend of increasing O2 partial pressures with increasing fluorine partial pressures during the depositions. This is attributed to the well known reaction: 2H2O+F2→O2+4HF. However, no trend in the measured water partial pressures can be observed. The increase in the O2 partial pressure is therefore attributed to a reaction between water and fluorine on the chamber walls. The chemical analysis show that the hydrogen incorporation in the films were lowered from ~10 at.% when deposited in the presence of water vapor to ~3 at.% when deposited in the presence of water vapor and 2×10-5 Torr fluorine. The hydrogen incorporation stabilize at ~3 at.% at higher fluorine partial pressures. However, there is also a large amount of fluorine incorporated in the films, ~20 at.% with a fluorine partial pressure during the deposition of 2×10-5 Torr and ~46 at.% with a fluorine partial pressure of 5×10-5 Torr. There is a slight increase in the aluminum concentration in the films deposited with fluorine. This is attributed to bonding the hydrogen in aluminum hydroxide while the reminder forms Al2O3 or Al leading to an increase in the aluminum concentration in the film. A linear decrease in the deposition rate with increasing fluorinepartial pressures during the deposition was observed, this can be explained by sputter etching of AlFx and AlOxFy by energetic O- ions. The XRD investigation show that the films deposited with the highest fluorine partial pressures were x-ray amorphous, the films with deposited with lower fluorine partial pressures are therefore also assumed to be amorphous.

Place, publisher, year, edition, pages
2009. , 31 p.
Keyword [en]
alumina, RF-sputtering, hydrogen, fluorine, amorphous alumina
Keyword [sv]
aluminiumoxid, RF-sputtering, väte, fluor, amorft aluminumoxid
National Category
Other Engineering and Technologies not elsewhere specified
URN: urn:nbn:se:liu:diva-16706ISRN: LITH-IFM-A-EX--09/2046--SEOAI: diva2:160272
2009-01-30, Röntgen, 58381 Linköping, Physics Building, 10:15 (English)
Available from: 2011-09-01 Created: 2009-02-12 Last updated: 2009-02-18Bibliographically approved

Open Access in DiVA

fulltext(1499 kB)318 downloads
File information
File name FULLTEXT01.pdfFile size 1499 kBChecksum SHA-512
Type fulltextMimetype application/pdf

Search in DiVA

By author/editor
Magnfält, Daniel
By organisation
Department of Physics, Chemistry and Biology
Other Engineering and Technologies not elsewhere specified

Search outside of DiVA

GoogleGoogle Scholar
Total: 318 downloads
The number of downloads is the sum of all downloads of full texts. It may include eg previous versions that are now no longer available

Total: 137 hits
ReferencesLink to record
Permanent link

Direct link