Residual stress formation in multilayered TiN/TaNx coatings during reactive magnetron sputter deposition
AB Sandvik Coromant, Stockholm, Sweden .
Materials Science Division, The Ångström Laboratory, Uppsala University, Uppsala, Sweden .
Linköping University, Department of Physics, Chemistry and Biology, Thin Film Physics. Linköping University, The Institute of Technology.
Linköping University, Department of Physics, Chemistry and Biology, Thin Film Physics. Linköping University, The Institute of Technology.
Show others and affiliations
2000 (English)In: Journal of Vacuum Science & Technology. A. Vacuum, Surfaces, and Films, ISSN 0734-2101, E-ISSN 1520-8559, Vol. 18, no 6, 2884-2889 p.Article in journal (Refereed) Published
Abstract [en]

Multilayered physical vapor deposited TiN/TaNx coatings were deposited on cemented carbide substrates using a dual target magnetron sputtering system. The coatings were investigated with respect to the influence of nitrogen partial pressure during deposition on the residual stress developed in the coatings. Furthermore, the fracture strength of the material, i.e., the magnitude of the tensile stress that the coating can support without cracking, was evaluated. It was found that, by increasing the nitrogen partial pressure, it is possible to change the stress from compressive to tensile. The highest tensile stress was about 3.6 GPa. Despite this high stress, the coating displayed no cracking. This implies that it is possible to grow TiN/TaNx multilayered coatings with high tensile fracture strength using dual magnetron sputtering and a high deposition temperature (about 680 °C). 

Place, publisher, year, edition, pages
2000. Vol. 18, no 6, 2884-2889 p.
National Category
Engineering and Technology
URN: urn:nbn:se:liu:diva-47552DOI: 10.1116/1.1308594OAI: diva2:268448
Available from: 2009-10-11 Created: 2009-10-11 Last updated: 2016-08-31
In thesis
1. Nanostructural design of transition metal nitride thin films
Open this publication in new window or tab >>Nanostructural design of transition metal nitride thin films
2005 (English)Doctoral thesis, comprehensive summary (Other academic)
Abstract [en]

Early transition metal nitrides have found extensive use in a range of thin film applications. We are just beginning to understand their growth from vapor phase deposition and microstructure-property relationships. There are large fields to explore, not the least for the nanoand microstructural design in materials offered by a developed deposition process control and alloying by additional elements to grow, e.g., ternary nitrides or superlattices. The work in this thesis has been directed towards increasing the fondarnental understanding of the synthesis, characterization, and properties for some technologically relevant nitrides. Binary and ternary phases of transition metal nitrides, as well as artificial superlattice structures have been studied. In order to prepare materials of high purity, film deposition was performed by Ultra-High Vacuum Reactive Magnetron Sputtering.

In this thesis single-crystal Ti2A1N(0001) thin films were synthesized by epitaxial growth onto MgO(111) substrates at elevated temperature and using a 2Ti:A1 compound sputtering target. This is the first thin film deposition process reported for a nitride of the so called Ma+1AXn phase family of compounds - an inherently nanolaminated material that is characterized by metallic conductivity and ductility with retained ceramic strength, high-temperature stability, oxidation, and corrosion resistance. Th2A1N is found to have a room-temperature resistivity of 39 μΩcm, Young's modulus of 16-17 GPa, and hardness of 210 GPa. It is also found that nitrogen-depleted deposition conditions yield the growth of equilibriwn phases TiA1, Ti3A1 and Ti3A1N. For overstoichiometric deposition conditions with respect to Ti2A1N, a phase mixture with TiN was obtained. A super-structure in the TiN phase was also observed to form along the [111] direction at a repetition distance of 7.34 Å, possibly related to A1 segregation.

CrN/ScN superlattices were designed for use as soft x-ray mirrors and investigated with respect to thermal stability, hardness, and x-ray reflectivity properties. The combined performance of as-deposited superlattices films, with a compositional modulation period of 1.64 nm, both as a mirror and for thermal and mechanical stability was found to be far better than state of the art metallic Cr/Sc multilayers. In fact, the obtained reflectance of 6.95% at a wavelength of 3.1 nm is excellent, the structure is intact after annealing above 800 °C, and the hardness of 19 GPa makes the mirror effectively scratch-proof.

Stress measurements in the TiN/TaN system were performed in-situ. The obtained results showed that a technique based on curvature measurements by laser deflection on the sample during thin film deposition works when employed at the elevated temperatures typically used for sputtering of nitrides. Findings from the in-situ measurements show a correlation between the stress and the film microstructure and the phase composition of TaN layers. It is also shown how the individual layers in an TiN/TaN artificial superlattice affects the stress with a sub-nm resolution. The contribution from thermal stress is also detected and the fine increase in temperature due to exposure of energetic particles from the plasma can be calculated from that stress.

A multiphase region in nitrides was demonstrated to form in the NbxZr1-xN model system. The existence of such a multiphase or polytypic structure is predicted by first-principles density functional theory calculations that to occur in nitrides of compositional regions with valence electron concentrations that yield the same total energy for different crystal structures. Films with varying composition were grown and transmission electron microscopy studies revealed an increase in defect density for the x= 0.5 composition. Nanoindentation performed on such films showed an increase in hardness of - 20% compared to the binary nitrides. Analysis of the indents revealed that materials volumes had rotated away from the indenter, thus offering an alternative mechanism for plastic deformation compared to glide on preferred slip systems seen in the cubic binary nitrides. The materials design concept of such phase stability tuning for mechanical strengthening by a high density of phase interfaces is proposed to be expanded to other materials systems.

Place, publisher, year, edition, pages
Linköping: Linköping University Electronic Press, 2005. 41 p.
Linköping Studies in Science and Technology. Dissertations, ISSN 0345-7524 ; 923
National Category
Natural Sciences
urn:nbn:se:liu:diva-28395 (URN)13531 (Local ID)91-85297-33-X (ISBN)13531 (Archive number)13531 (OAI)
Public defence
2005-02-18, Planck, Fysikhuset, Campus Valla, Linköpings Universitet, Linköping, 14:00 (English)
Available from: 2009-10-09 Created: 2009-10-09 Last updated: 2012-11-28Bibliographically approved

Open Access in DiVA

No full text

Other links

Publisher's full text

Search in DiVA

By author/editor
Joelsson, TorbjörnBirch, JensHultman, Lars
By organisation
Thin Film PhysicsThe Institute of Technology
In the same journal
Journal of Vacuum Science & Technology. A. Vacuum, Surfaces, and Films
Engineering and Technology

Search outside of DiVA

GoogleGoogle Scholar
The number of downloads is the sum of all downloads of full texts. It may include eg previous versions that are now no longer available

Altmetric score

Total: 102 hits
ReferencesLink to record
Permanent link

Direct link