liu.seSearch for publications in DiVA
Change search
CiteExportLink to record
Permanent link

Direct link
Cite
Citation style
  • apa
  • harvard1
  • ieee
  • modern-language-association-8th-edition
  • vancouver
  • oxford
  • Other style
More styles
Language
  • de-DE
  • en-GB
  • en-US
  • fi-FI
  • nn-NO
  • nn-NB
  • sv-SE
  • Other locale
More languages
Output format
  • html
  • text
  • asciidoc
  • rtf
Electronic-grade GaN(0001)/Al2O3(0001) grown by reactive DC-magnetron sputter epitaxy using a liquid Ga target
Linköping University, Department of Physics, Chemistry and Biology. Linköping University, The Institute of Technology.
Linköping University, Department of Physics, Chemistry and Biology. Linköping University, The Institute of Technology.
Linköping University, Department of Physics, Chemistry and Biology, Thin Film Physics. Linköping University, The Institute of Technology.ORCID iD: 0000-0003-3203-7935
Linköping University, Department of Physics, Chemistry and Biology. Linköping University, The Institute of Technology.
Show others and affiliations
2011 (English)In: Applied Physics Letters, ISSN 0003-6951, E-ISSN 1077-3118, Vol. 98, no 14, 141915- p.Article in journal (Refereed) Published
Abstract [en]

Electronic-grade GaN (0001) epilayers have been grown directly on Al2O3 (0001) substrates by reactive DC-magnetron sputter epitaxy (MSE) from a liquid Ga sputtering target in an Ar/N2 atmosphere. The as-grown GaN epitaxial film exhibit low threading dislocation density on the order of ≤ 1010 cm-2 obtained by transmission electron microscopy and modified Williamson-Hall plot. X-ray rocking curve shows narrow fullwidth at half maximum (FWHM) of 1054 arcsec of the 0002 reflection. A sharp 4 K photoluminescence peak at 3.474 eV with a FWHM of 6.3 meV is attributed to intrinsic GaN band edge emission. The high structural and optical qualities indicate that MSEgrown GaN epilayers can be used for fabricating high-performance devices without the need of any buffer layer.

Place, publisher, year, edition, pages
American Institute of Physics , 2011. Vol. 98, no 14, 141915- p.
Keyword [en]
GaN, DC-MSE, Sputtering, ERDA, TEM, XRD, PL
National Category
Natural Sciences
Identifiers
URN: urn:nbn:se:liu:diva-65724DOI: 10.1063/1.3576912ISI: 000289297800030OAI: oai:DiVA.org:liu-65724DiVA: diva2:398537
Note
On the day of the defence date the status of this article was: Manuscript. Original Publication: Muhammad Junaid, Ching-Lien Hsiao, Justinas Palisaitis, Jens Jensen, Per Persson, Lars Hultman and Jens Birch, Electronic-grade GaN(0001)/Al2O3(0001) grown by reactive DC-magnetron sputter epitaxy using a liquid Ga target, 2011, Applied Physics Letters, (98), 14, 141915. http://dx.doi.org/10.1063/1.3576912 Copyright: American Institute of Physics http://www.aip.org/ Available from: 2011-02-18 Created: 2011-02-18 Last updated: 2017-12-11Bibliographically approved
In thesis
1. Magnetron Sputter Epitaxy of GaN
Open this publication in new window or tab >>Magnetron Sputter Epitaxy of GaN
2011 (English)Licentiate thesis, comprehensive summary (Other academic)
Abstract [en]

Electronic-grade GaN (0001) epilayers have been grown directly on Al2O3 (0001) substrates by reactive DC-magnetron sputter epitaxy (MSE) from a liquid Ga sputtering target in an Ar/N2 atmosphere. The as-grown GaN epitaxial film exhibit low threading dislocation density on the order of ≤ 1010 cm-2 obtained by transmission electron microscopy and modified Williamson-Hall plot. X-ray rocking curve shows narrow fullwidth at half maximum (FWHM) of 1054 arcsec of the 0002 reflection. A sharp 4 K photoluminescence peak at 3.474 eV with a FWHM of 6.3 meV is attributed to intrinsic GaN band edge emission. The high structural and optical qualities indicate that MSEgrown GaN epilayers can be used for fabricating high-performance devices without the need of any buffer layer. GaN (0001) thin films were grown on Al2O3 substrates by reactive high power impulse magnetron sputtering of liquid Ga targets in a mixed N2/Ar discharge. A combination of x-ray diffraction, electron microscopy, atomic force microscopy, μ-Raman microscopy, photoluminescence, time of flight elastic recoil detection, and cathodoluminescence showed the formation of both relaxed and strained domains in the same films. . While the strained domains form due to ion bombardment during growth. The relaxed domains exhibit superior structural and optical properties comparative to the strained domains, including room temperature luminescence.

Place, publisher, year, edition, pages
Linköping: Linköping University Electronic Press, 2011. 35 p.
Series
Linköping Studies in Science and Technology. Thesis, ISSN 0280-7971 ; 1470
National Category
Natural Sciences
Identifiers
urn:nbn:se:liu:diva-65729 (URN)978-91-7393-226-4 (ISBN)
Presentation
2011-03-03, Planck, Fysikhuset, Campus Valla, Linköpings universitet, Linköping, 10:15 (English)
Opponent
Supervisors
Available from: 2011-02-18 Created: 2011-02-18 Last updated: 2016-08-31Bibliographically approved
2. Magnetron Sputter Epitaxy of GaN Epilayers and Nanorods
Open this publication in new window or tab >>Magnetron Sputter Epitaxy of GaN Epilayers and Nanorods
2012 (English)Doctoral thesis, comprehensive summary (Other academic)
Abstract [en]

In this research, electronic-grade GaN(0001) epilayers and nanorods have been grown onto Al2O3(0001) and Si(111) substrates, respectively, by reactive magnetron sputter epitaxy (MSE) using liquid Ga as a sputtering target. MSE, employing ultra high vacuum conditions, high-purity source materials, and lowenergy ion assisted deposition from substrate biasing, is a scalable method, lending itself to large area GaN synthesis.

For the growth of epitaxial GaN films two types of sputtering techniques, direct current (DC) magnetron sputtering and high power impulse magnetron sputtering (HiPIMS) were studied. The GaN epitaxial films grown by DC-MSE directly on to Al2O3(0001) in a mixture of Ar and N2, feature low threading dislocation densities on the order of ≤ 1010 cm-2, as determined by transmission electron microscopy (TEM) and modified Williamson-Hall plots. X-ray rocking curves reveal a narrow full-width at half maximum (FWHM) of 1054 arcsec of the 0002 reflection. A sharp 4 K photoluminescence (PL) peak at 3.474 eV with a FWHM of 6.3 meV is attributed to intrinsic GaN band edge emission. GaN(0001) epitaxial films grown on Al2O3 substrates by HiPIMS deposition in a mixed N2/Ar discharge contain both strained domains and almost relaxed domains in the same epilayers, which was determined by a combination of x-ray diffraction (XRD), TEM, atomic force microscopy (AFM), μ-Raman microscopy, μ-PL, and Cathodoluminescence (CL). The almost fully relaxed domains show superior structural and optical properties evidenced by a rocking curves with full width at half maximum of 885 arc sec and a low temperature band edge luminescence at 3.47 eV with the FWHM of 10 meV. The other domain exhibits a 14 times higher isotropic strain component, which is due to higher densities of point and extended defects, resulting from  bombardment of energetic species during growth.

Single-crystal GaN(0001) nanorods have been grown directly on Si(111) substrates by DC-MSE in a pure N2environment. The as-grown GaN nanorods exhibit very high crystal quality from bottom to the top without any stacking faults, as determined by TEM. The crystal quality is found to increase with increasing working pressure. XRD results show that all the rods are highly 0001 oriented. All nanorods exhibit an N-polarity, as determined by convergent beam electron diffraction methods. Sharp and well-resolved 4 K μ-PL peaks at ~3.474 eV with a FWHM ranging from 1.7 meV to 22 meV are attributed to the intrinsic GaN band edge emission and corroborate the exceptional crystal quality of the material. Texture measurements reveal that the rods have random in-plane orientation when grown on Si(111) with its native oxide while they have an inplane epitaxial relationship of GaN[11̅20] // Si[1̅10] when grown on Si(111) without the surface oxide. The best structural and optical properties of the rods were achieved at N2 partial pressures of 15 to 20 mTorr. By diluting the reactive N2 working gas in DC-MSE with Ar, it is possible to achieve favorable growth conditions for high quality GaN nanorods onto Si(111) at a low total pressure of 5 mTorr. With an addition of small amount of Ar (0.5 mTorr), we observe an increase in nanorod aspect ratio from 8 to ~35, a decrease in average diameter from 74 nm to 35 nm, and a 2-fold increase in nanorod density compared to pure N2 conditions. By further dilution, the aspect ratio continuously decreases to 14 while the diameter increases to 60 nm and the nanorod density increases to a maximum of 2.4×109 cm-1. The changes in nanorod morphology upon Ar-dilution of the N2 working gas are explained by a transition from N-rich growth conditions, promoting the diffusion induced nanorods growth mode, to Ga-rich growth conditions, in qualitative agreement with GaN nanorods growth by MBE. At N2 partial pressure of 2.5 mTorr, the Ga-target is close to a non-poisoned state which gives the most perfect crystal quality which is reflected in an exceptionally narrow band edge emission at 3.479 eV with a FWHM of only 1.7 meV. Such structural and optical properties are comparable to rods previously grown at 3 to 4 time higher total working pressures of pure N2.

Place, publisher, year, edition, pages
Linköping: Linköping University Electronic Press, 2012. 66 p.
Series
Linköping Studies in Science and Technology. Dissertations, ISSN 0345-7524 ; 1482
National Category
Natural Sciences
Identifiers
urn:nbn:se:liu:diva-84655 (URN)978-91-7519-782-1 (ISBN)
Public defence
2012-11-05, Planck, Fysikhuset, Campus Valla, Linköpings universitet, Linköping, 10:15 (English)
Opponent
Supervisors
Available from: 2012-10-16 Created: 2012-10-16 Last updated: 2016-08-31Bibliographically approved

Open Access in DiVA

fulltext(794 kB)773 downloads
File information
File name FULLTEXT01.pdfFile size 794 kBChecksum SHA-512
8328aed2ed91840cf86b0544ed70e8389dd436fc553673fa5e8e259c6cc275aee856745db5244f3ee565d7584ef3ec58fee0cda906f72dd0ea539d9ec1f425ad
Type fulltextMimetype application/pdf

Other links

Publisher's full text

Authority records BETA

Junaid, MuhammadHsiao, Ching-LienPalisaitis, JustinasJensen, JensPersson, PerHultman, LarsBirch, Jens

Search in DiVA

By author/editor
Junaid, MuhammadHsiao, Ching-LienPalisaitis, JustinasJensen, JensPersson, PerHultman, LarsBirch, Jens
By organisation
Department of Physics, Chemistry and BiologyThe Institute of TechnologyThin Film Physics
In the same journal
Applied Physics Letters
Natural Sciences

Search outside of DiVA

GoogleGoogle Scholar
Total: 773 downloads
The number of downloads is the sum of all downloads of full texts. It may include eg previous versions that are now no longer available

doi
urn-nbn

Altmetric score

doi
urn-nbn
Total: 536 hits
CiteExportLink to record
Permanent link

Direct link
Cite
Citation style
  • apa
  • harvard1
  • ieee
  • modern-language-association-8th-edition
  • vancouver
  • oxford
  • Other style
More styles
Language
  • de-DE
  • en-GB
  • en-US
  • fi-FI
  • nn-NO
  • nn-NB
  • sv-SE
  • Other locale
More languages
Output format
  • html
  • text
  • asciidoc
  • rtf