Influence of Shot Peening Parameters on Residual Stresses in Flake and Vermicular Cast Irons
Linköping University, Department of Management and Engineering, Engineering Materials. Linköping University, The Institute of Technology.
Linköping University, Department of Management and Engineering, Engineering Materials. Linköping University, The Institute of Technology.
Base Engine & Materials Technology, Volvo Powertrain, Göteborg.
Testing Methods and Testing, Scania CV AB, Södertälje.
Show others and affiliations
2014 (English)Conference paper (Refereed)
Abstract [en]

Test samples of grey and compacted graphite cast irons with pearlitic matrix were shot-peened to different surface conditions using twelve different combinations of shot size, peening intensity and peening coverage percentage. Relatively high surface compressive residual stresses varying between 245 to 565 MPa were observed and the compressive residual stresses reached a depth between 280 µm and 770 µm. Within the range of peening parameters used, the compacted graphite cast iron with its vermicular graphite showed a somewhat better response to the same shot-peening treatment than the grey cast iron containing flake graphite, giving a larger peening affected zone with higher compressive residual stresses. For both the cast irons, an increase in peening coverage percentage, shot size or peening intensity led often to a lower surface compressive stress. However, peening using a higher intensity greatly increased the degree and extent of plastic deformation and therefore increased the magnitude and penetration depth of the subsurface compressive residual stresses, while the effect of increasing shot size also depends on the peening intensity. On the other hand, measurements on the grey cast iron samples showed that the peening coverage has little effect on the depth profile of residual stress.

Place, publisher, year, edition, pages
Trans Tech Publications Inc., 2014. Vol. 768-769, 534-541 p.
National Category
Engineering and Technology Materials Engineering
URN: urn:nbn:se:liu:diva-89578DOI: 10.4028/ 000336693000070OAI: diva2:608333
International Conference on Residual Stresses 9 (ICRS 9), Garmisch-Partenkirchen, Germany, 7 – 9 October 2012
Available from: 2013-03-13 Created: 2013-02-27 Last updated: 2014-12-10Bibliographically approved

Open Access in DiVA

fulltext(2836 kB)4573 downloads
File information
File name FULLTEXT01.pdfFile size 2836 kBChecksum SHA-512
Type fulltextMimetype application/pdf

Other links

Publisher's full text

Search in DiVA

By author/editor
Lundberg, MattiasPeng, RuJohansson, Sten
By organisation
Engineering MaterialsThe Institute of Technology
Engineering and TechnologyMaterials Engineering

Search outside of DiVA

GoogleGoogle Scholar
Total: 4573 downloads
The number of downloads is the sum of all downloads of full texts. It may include eg previous versions that are now no longer available

Altmetric score

Total: 122 hits
ReferencesLink to record
Permanent link

Direct link