Luminescence of Acceptors in Mg-Doped GaN
Linköping University, Department of Physics, Chemistry and Biology, Semiconductor Materials. Linköping University, The Institute of Technology.
Linköping University, Department of Physics, Chemistry and Biology, Thin Film Physics. Linköping University, The Institute of Technology.
Linköping University, Department of Physics, Chemistry and Biology, Thin Film Physics. Linköping University, The Institute of Technology.ORCID iD: 0000-0002-9840-7364
Linköping University, Department of Physics, Chemistry and Biology, Semiconductor Materials. Linköping University, The Institute of Technology.
Show others and affiliations
2013 (English)In: Japanese Journal of Applied Physics, ISSN 0021-4922, E-ISSN 1347-4065, Vol. 52, no 8Article in journal (Refereed) Published
Abstract [en]

Recent photoluminescence (PL) data for Mg-doped GaN at 2 K are discussed, with reference to published theoretical calculations of the electronic level structure. It is concluded that the typical PL peaks at 3.466 eV (acceptor bound exciton ABE1) and the broader 3.27 eV donor-acceptor pair (DAP) PL are the expected standard PL signatures of the substitutional Mg acceptor. Additional broader peaks at 3.455 eV (ABE2) and 3.1 eV are suggested to be related to the same acceptors perturbed by nearby basal plane stacking faults. The low temperature metastability of PL spectra is assigned to a nonradiative metastable deep level.

Place, publisher, year, edition, pages
Japan Society of Applied Physics , 2013. Vol. 52, no 8
National Category
Engineering and Technology
URN: urn:nbn:se:liu:diva-98151DOI: 10.7567/JJAP.52.08JJ03ISI: 000323883100123OAI: diva2:652285

Funding Agencies|K. A. Wallenberg Foundation||Swedish Energy Agency||Li-Li NFM Center at Linkoping University||

Available from: 2013-09-30 Created: 2013-09-30 Last updated: 2016-08-31
In thesis
1. Doping effects on the structural and optical properties of GaN
Open this publication in new window or tab >>Doping effects on the structural and optical properties of GaN
2013 (English)Doctoral thesis, comprehensive summary (Other academic)
Abstract [en]

Today there is a strong drive towards higher efficiency light emitters and devices for power electronics based on GaN and its ternary compounds. Device performance can be improved in several ways on the material level. Development of bulk GaN to substitute sapphire and SiC as substrate materials can allow lower defect density epitaxial GaN layers to be grown. Using nonpolar homoepitaxial layers alleviates the problem of polarization fields present in polar GaN epilayers. This thesis advances the field by attacking outstanding problems related to doping and its influence on structural and optical properties of GaN. Optical and structural investigations were performed on bulk GaN grown by halide vapor phase epitaxy (HVPE) and on polar and nonpolar epitaxial GaN grown by metal organic chemical vapor deposition (MOCVD), doped with different impurities: Mg, Si, O or C. Optical characterization was done using photoluminescence (PL), time-resolved photoluminescence (TRPL), and cathodoluminescence (CL) in-situ scanning electron microscope, whereas structural properties were studied by means of transmission electron microscopy (TEM) and atom probe tomography (APT).

A correlation between Mg doping levels and stacking fault (SF) concentration in highly Mg-doped c-plane homoepitaxial GaN layers is found. Increasing Mg concentrations, from 2×1018 cm-3 to 5×1019 cm-3, coincides with increasing density of small, 3-10 nm-sized, SFs. Emission lines ascribed to SFs are observed in CL in all the studied samples. The observed SF-related luminescence can be explained by a model where Mg atoms interacting with the nearby SF changes the confinement for holes and leads to a pronounced defectrelated luminescence. Non-polar m-plane homoepitaxial GaN layers with Mg concentration of 2×1018 cm-3 and 3×1019 cm-3 exhibits high density of basal SFs as well as a number of prismatic SFs. Instead of normally observed in nonpolar GaN SF-related broad lines several sharp lines are detected in the 3.36-3.42 eV region. Their relation to donor-acceptor pair recombination (DAP) was dismissed by calculating the DAP energies and fitting with the measured spectra. The sharp lines are tentatively explained by some impurities bound to point defects or SFs. The origin of two Mg related acceptor bound exciton (ABE) peaks in the emission spectra is also proposed: narrower ABE1 peak at 3.466 eV is identified as coming from a substitutional Mg atom. Broader emission at 3.454 eV is deemed to be coming from a Mg acceptor atom perturbed by a nearby SF. Additionally, Mg cluster formation in the highest doped sample ([Mg] = 1×1020 cm-3) was revealed by APT.

Simultaneous doping by Si and O was studied for HVPE grown bulk GaN. Doping with O concentration from 1017 cm-3 leads to a decrease in the Si concentration to less than 1016 cm-3. Si incorporation is believed to be suppressed by the competing Ga-vacancy-O incorporation process. Bandgap narrowing by 6 meV due to high doping was observed. Donor bound exciton (DBE) lifetime was obtained from TPRL experimental data and it is found to decrease with increasing doping. In non-polar m-plane homoepitaxial GaN Si doping influences the SF-related luminescence. At moderate Si concentrations excitons are bound to the impurity atoms or impurity-SF complex. Proximity of impurity atoms changes the potential for SF creating localization for charge carriers resulting in SF-related emission. At dopant concentrations higher than the Mott limit screening destroys the carrier interaction and, thus, the exciton localization at impurity-SF complex.

Finally, C-doped HVPE grown bulk GaN layers were studied by TEM, CL, and TRPL. Enhanced yellow line (YL) luminescence was observed with increasing C doping. Stability of YL in a wide temperature range (5-300 K) confirms that YL is due to a deep defect, likely CN-ON complex. Low-temperature CL mapping reveals a pit-like structure with different luminescence properties in different areas. DBE emission dominates in CL spectra within the pits while in pit-free areas, in contrast, two ABE lines typical for Mg-doped GaN are observed.

Place, publisher, year, edition, pages
Linköping: Linköping University Electronic Press, 2013. 54 p.
Linköping Studies in Science and Technology. Dissertations, ISSN 0345-7524 ; 1554
National Category
Natural Sciences
urn:nbn:se:liu:diva-100760 (URN)10.3384/diss.diva-100760 (DOI)978-91-7519-483-7 (print) (ISBN)
Public defence
2013-12-12, Planck, Fysikhuset, Campus Valla, Linköpings universitet, Linköping, 10:15 (English)
Available from: 2013-11-11 Created: 2013-11-11 Last updated: 2016-08-31Bibliographically approved

Open Access in DiVA

fulltext(283 kB)462 downloads
File information
File name FULLTEXT01.pdfFile size 283 kBChecksum SHA-512
Type fulltextMimetype application/pdf

Other links

Publisher's full text

Search in DiVA

By author/editor
Monemar, BoKhromov, SergeyPozina, GaliaPaskov, PlamenBergman, PederHemmingsson, CarlHultman, Lars
By organisation
Semiconductor MaterialsThe Institute of TechnologyThin Film Physics
In the same journal
Japanese Journal of Applied Physics
Engineering and Technology

Search outside of DiVA

GoogleGoogle Scholar
Total: 462 downloads
The number of downloads is the sum of all downloads of full texts. It may include eg previous versions that are now no longer available

Altmetric score

Total: 182 hits
ReferencesLink to record
Permanent link

Direct link