Mo2TiAlC2: A new ordered layered ternary carbide
2015 (English)In: Scripta Materialia, ISSN 1359-6462, E-ISSN 1872-8456, Vol. 101, 5-7 p.Article in journal (Refereed) Published
Herein we report on the synthesis of a new layered ternary carbide, Mo2TiAlC2, that was synthesized by heating an elemental mixture at 1600 degrees C for 4 h under an Ar flow. Its hexagonal, a and c lattice parameters were calculated via Rietveld analysis of powder X-ray diffraction patterns to be, respectively, 2.997 angstrom and 18.661 angstrom. High-resolution scanning transmission electron microscopy showed that this phase is ordered, with Ti layers sandwiched between two Mo layers in a M(3)AX(2) type ternary carbide structure. (C) 2015 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
Place, publisher, year, edition, pages
Elsevier , 2015. Vol. 101, 5-7 p.
Ordered MAX phases; Ternary carbides; Molybdenum carbides; High resolution scanning transmission electron microscopy
IdentifiersURN: urn:nbn:se:liu:diva-117200DOI: 10.1016/j.scriptamat.2014.12.024ISI: 000350932800002OAI: oai:DiVA.org:liu-117200DiVA: diva2:807236
Funding Agencies|Army Research Office (United States) [W911NF-11-1-0525, W911NF-14-1-0568]; SSF synergy grant FUNCASE Functional Carbides and Advanced Surface Engineering Sweden; Knut and Alice Wallenberg Foundation2015-04-232015-04-212016-08-31