Single Domain 3C-SiC Growth on Off-Oriented 4H-SiC Substrates
Linköping University, Department of Physics, Chemistry and Biology, Semiconductor Materials. Linköping University, Faculty of Science & Engineering.
Linköping University, Department of Physics, Chemistry and Biology, Semiconductor Materials. Linköping University, Faculty of Science & Engineering.
Linköping University, Department of Physics, Chemistry and Biology, Semiconductor Materials. Linköping University, Faculty of Science & Engineering.
Linköping University, Department of Physics, Chemistry and Biology, Semiconductor Materials. Linköping University, Faculty of Science & Engineering.ORCID iD: 0000-0003-1000-0437
Show others and affiliations
2015 (English)In: Crystal Growth & Design, ISSN 1528-7483, E-ISSN 1528-7505, Vol. 15, no 6, 2940-2947 p.Article in journal (Refereed) Published
Abstract [en]

We investigated the formation of structural defects in thick (∼1 mm) cubic silicon carbide (3C-SiC) layers grown on off-oriented 4H-SiC substrates via a lateral enlargement mechanism using different growth conditions. A two-step growth process based on this technique was developed, which provides a trade-off between the growth rate and the number of defects in the 3C-SiC layers. Moreover, we demonstrated that the two-step growth process combined with a geometrically controlled lateral enlargement mechanism allows the formation of a single 3C-SiC domain which enlarges and completely covers the substrate surface. High crystalline quality of the grown 3C-SiC layers is confirmed using high resolution X-ray diffraction and low temperature photoluminescence measurements.

Place, publisher, year, edition, pages
American Chemical Society (ACS), 2015. Vol. 15, no 6, 2940-2947 p.
National Category
Materials Chemistry
URN: urn:nbn:se:liu:diva-118525DOI: 10.1021/acs.cgd.5b00368ISI: 000355890400051OAI: diva2:815338

Swedish Energy Agency; Swedish Research Council; Swedish Governmental Agency for Innovation Systems (Vinnova)

Available from: 2015-05-29 Created: 2015-05-29 Last updated: 2016-05-13
In thesis
1. Sublimation Growth of 3C-SiC: From Thick Layers to Bulk Material
Open this publication in new window or tab >>Sublimation Growth of 3C-SiC: From Thick Layers to Bulk Material
2016 (English)Doctoral thesis, comprehensive summary (Other academic)
Abstract [en]

Silicon carbide (SiC) is a semiconductor material which holds high promises for various device applications. It can be obtained in different crystal structures called polytypes. The most common ones are hexagonal (6H- and 4H-SiC) and cubic (3C-SiC) silicon carbide. The 6H- and 4H-SiC single crystal substrates are commercially available, while technologies for the growth of 3C-SiC are still under development. The unique 3C-SiC properties like isotropy, narrower bandgap (2.4 eV)  compared to hexagonal polytypes (about 3 eV) and high electron mobility make it better over hexagonal counterparts for some semiconductor applications, for example, metal oxide semiconductor field effect transistors (MOSFETs). However, due to lack of high quality material, the full potential of 3C-SiC in device applications has not been revealed. In addition, it has properties suitable to explore new concepts in efficient photovoltaics or solar driven hydrogen generation by water splitting.

There is a need for 3C-SiC seeds to grow large 3C-SiC crystals by the widely used Physical Vapor Transport (PVT) technique. In case of hexagonal SiC polytypes such seeds were produced by the Lely method during which hexagonal SiC crystals spontaneously nucleate on the inner walls of a crucible. However, the formation of 3C-SiC using the Lely method is rarely observed. Therefore, the 3C-SiC has to be heteroepitaxially grown on silicon or hexagonal SiC substrates. Silicon is an inexpensive material with very high crystalline quality. However, due to almost 20% mismatch in lattice parameters and 8% difference in thermal expansion coefficient there is a high density of structural defects formed at the 3C-SiC/Si interface. In contrast, the 3C-SiC/hexagonal SiC material system does not encounter such problems, but there are other challenges like polytype stability or formation of structural defects called double positioning boundaries (DPBs).

This thesis work mainly focuses on the growth of 3C-SiC on hexagonal SiC substrates using sublimation epitaxy. The research covers the development of growth process for thick (~1 mm) 3C-SiC layers, advancement of the growth process to eliminate DPBs and growth of bulk material using thick 3C-SiC layers as seeds. The 3C-SiC was grown on off-oriented hexagonal SiC substrates. The surfaces of such substrates contain high density of steps. Therefore, they have mostly been used for the growth of homoepitaxial hexagonal layers or bulk crystals via step flow mechanism. However, as demonstrated in this thesis, under special conditions the 3C-SiC with high crystalline quality can also be grown on off-oriented hexagonal substrates. The stability window for the growth of hexagonal and cubic polytypes on nominally on-axis hexagonal SiC substrates is also explored. Moreover, it is demonstrated how the temperature profile inside the graphite crucible is influenced by the change in thermal insulation properties and how such change results in enhanced polytype stability during the growth of thick SiC layers. In addition, different sources for sublimation epitaxial growth of doped SiC layers were analyzed to gain further understanding of new parameter windows.

As a part of this thesis, a sublimation etching of 6H-, 4H- and 3C-SiC polytypes is presented using two different etching arrangements in vacuum (10-5 mbar) and Ar ambient. It is demonstrated that this technique can be used to remove residual scratches on the surface as well as to obtain various surface step structures which could be used for the growth of graphene nanostructures.

Place, publisher, year, edition, pages
Linköping: Linköping University Electronic Press, 2016. 45 p.
Linköping Studies in Science and Technology. Dissertations, ISSN 0345-7524 ; 1760
National Category
Physical Sciences
urn:nbn:se:liu:diva-127802 (URN)978-91-7685-778-6 (Print) (ISBN)
Public defence
2016-06-09, Planck, Fysikhuset, Campus Valla, Linköping, 10:15 (English)
Available from: 2016-05-13 Created: 2016-05-13 Last updated: 2016-05-13Bibliographically approved

Open Access in DiVA

fulltext(1563 kB)27 downloads
File information
File name FULLTEXT01.pdfFile size 1563 kBChecksum SHA-512
Type fulltextMimetype application/pdf

Other links

Publisher's full text

Search in DiVA

By author/editor
Jokubavicius, ValdasYazdi, Gholam RezaLiljedahl, RickardIvanov, Ivan GueorguievSun, JianwuLiu, XinyuYakimova, RositsaSyväjärvi, Mikael
By organisation
Semiconductor MaterialsFaculty of Science & Engineering
In the same journal
Crystal Growth & Design
Materials Chemistry

Search outside of DiVA

GoogleGoogle Scholar
Total: 27 downloads
The number of downloads is the sum of all downloads of full texts. It may include eg previous versions that are now no longer available

Altmetric score

Total: 214 hits
ReferencesLink to record
Permanent link

Direct link