Hot Corrosion Behavior of HVOF-sprayed CoNiCrAlYSi Coatings in a Sulphate Environment
Linköping University, Department of Management and Engineering.
Linköping University, Department of Management and Engineering.
Finspang, Sweden. (Siemens Industrial Turbomachinery AB, Finspång)
Linköping University, Department of Management and Engineering.
2015 (English)In: Vacuum, ISSN 0042-207X, E-ISSN 1879-2715, Vol. 122, no part A, 47-53 p.Article in journal (Refereed) Published
Abstract [en]

HVOF-sprayed CoNiCrAlYSi coatings were tested at 900 °C in a hot corrosion environment containing sodium–potassium sulphates. The HVOF spraying caused the typical splat-on-splat structure. The results after the hot corrosion testing showed that the corrosion preferentially occurred at the coating surface and the splat boundaries. The oxidation along the splat boundaries can isolate the splat from the underlying coating matrix. In those isolated splats or coating parts, internal oxidation and nitridation of Al took place, following that the Al-depleted coating fragments were then oxidized to spinels. For those coatings which had a worse splat boundary quality (i.e. with higher porosity and intersplat oxides) or had a worse coating surface quality (i.e. with more small coating fragments therefore more interfaces), heavier corrosion attack was observed on those coatings due to the corrosion of the splats or the coating fragments. The results indicated that the as-sprayed coating quality including porosity and surface morphology was important for the hot-corrosion resistance of the coatings.

Place, publisher, year, edition, pages
Elsevier, 2015. Vol. 122, no part A, 47-53 p.
Keyword [en]
Hot corrosion, sulphate, MCrAIY, HVOF
National Category
Corrosion Engineering
Identifiers
URN: urn:nbn:se:liu:diva-121840DOI: 10.1016/j.vacuum.2015-09-015OAI: oai:DiVA.org:liu-121840DiVA: diva2:859952
Available from: 2015-10-09 Created: 2015-10-09 Last updated: 2015-10-16

Open Access in DiVA

No full text

Other links

Publisher's full text

Search in DiVA

By author/editor
Peng, RuJohansson, Sten
By organisation
Department of Management and Engineering
In the same journal
Vacuum
Corrosion Engineering

Search outside of DiVA

GoogleGoogle Scholar
The number of downloads is the sum of all downloads of full texts. It may include eg previous versions that are now no longer available

Altmetric score

Total: 126 hits
ReferencesLink to record
Permanent link

Direct link