Structural defects are detrimental to the efficiency and quality of optoelectronic semiconductor devices. In this work, we study InGaN platelets with a quantum well structure intended for nano-LEDs emitting red light and how their optical properties, measured with cathodoluminescence, relate to the corresponding atomic structure. Through a method of spectroscopy-thinning-imaging, we demonstrate in plan-view how stacking mismatch boundaries intersect the quantum well in a pattern correlated with the observed diminished cathodoluminescence intensity. The results highlight the importance of avoiding stacking mismatch in small LED structures due to the relatively large region of non-radiative recombination caused by the mismatch boundaries.

This study presents a novel approach to forming low-resistance ohmic contacts for AlGaN/GaN HEMTs. The optimized contacts exhibit an outstanding contact resistance of approximately 0.15 & omega;& BULL;mm. This is achieved by firstly recessing the barrier of the heterostructure to a depth beyond the channel. In this way, the channel region is exposed on the sidewall of the recess. The coverage of the Ti/Al/Ti ohmic metalization on the sidewall is ensured through tilting of the sample during evaporation. The annealing process is performed at a low temperature of 550 & DEG;C. The approach does not require precise control of the recess etching. Furthermore, the method is directly applicable to most barrier designs in terms of thickness and Al-concentration. The impact of recessed sidewall angle, thickness and ratio of Ti and Al layers, and the annealing procedure are investigated. Structural and chemical analyses of the interface between the ohmic contacts and epi-structure indicate the formation of ohmic contacts by the extraction of nitrogen from the epi-structure. The approach is demonstrated on HEMT-structures with two different barrier designs in terms of Al-concentration and barrier thickness. The study demonstrate large process window in regard to recess depth and duration of the annealing as well as high uniformity of the contact resistance across the samples, rendering the approach highly suitable for industrial production processes.

Compositionally graded channel AlGaN/GaN high electron mobility transistors (HEMTs) offer a promising route to improve device linearity, which is necessary for low-noise radio-frequency amplifiers. In this work, we demonstrate different grading profiles of a 10-nm-thick AlxGa1-xN channel from x = 0 to x = 0.1 using hot-wall metal-organic chemical vapor deposition (MOCVD). The growth process is developed by optimizing the channel grading and the channel-to-barrier transition. For this purpose, the Al-profiles and the interface sharpness, as determined from scanning transmission electron microscopy combined with energy-dispersive x-ray spectroscopy, are correlated with specific MOCVD process parameters. The results are linked to the channel properties (electron density, electron mobility, and sheet resistance) obtained by contactless Hall and terahertz optical Hall effect measurements coupled with simulations from solving self-consistently Poisson and Schrodinger equations. The impact of incorporating a thin AlN interlayer between the graded channel and the barrier layer on the HEMT properties is investigated and discussed. The optimized graded channel HEMT structure is found to have similarly high electron density (similar to 9 x 10(12) cm(-2)) as the non-graded conventional structure, though the mobility drops from similar to 2360 cm(2)/V s in the conventional to similar to 960 cm(2)/V s in the graded structure. The transconductance g(m) of the linearly graded channel HEMTs is shown to be flatter with smaller g(m) and g(m) as compared to the conventional non-graded channel HEMT implying improved device linearity. (c) 2023 Author(s). All article content, except where otherwise noted, is licensed under a Creative Commons Attribution (CC BY) license (http://creativecommons.org/licenses/by/4.0/).

The hot-wall metalorganic chemical vapor deposition (MOCVD) concept, previously shown to enable superior material quality and high performance devices based on wide bandgap semiconductors, such as Ga(Al)N and SiC, has been applied to the epitaxial growth of beta-Ga2O3. Epitaxial beta-Ga2O3 layers at high growth rates (above 1 mu m/h), at low reagent flows, and at reduced growth temperatures (740 degrees C) are demonstrated. A high crystalline quality epitaxial material on a c-plane sapphire substrate is attained as corroborated by a combination of x-ray diffraction, high-resolution scanning transmission electron microscopy, and spectroscopic ellipsometry measurements. The hot-wall MOCVD process is transferred to homoepitaxy, and single-crystalline homoepitaxial beta-Ga2O3 layers are demonstrated with a 201 rocking curve width of 118 arc sec, which is comparable to those of the edge-defined film-fed grown (201) beta-Ga2O3 substrates, indicative of similar dislocation densities for epilayers and substrates. Hence, hot-wall MOCVD is proposed as a prospective growth method to be further explored for the fabrication of beta-Ga2O3.

The impact on the performance of GaN high electron mobility transistors (HEMTs) of in situ ammonia (NH3) pre-treatment prior to the deposition of silicon nitride (SiN) passivation with low-pressure chemical vapor deposition (LPCVD ) is investigated. Three different NH3 pre-treatment durations (0, 3, and 10 min) were compared in terms of interface properties and device performance. A reduction of oxygen (O) at the interface between SiN and epi-structure is detected by scanning transmission electron microscopy (STEM )-electron energy loss spectroscopy (EELS) measurements in the sample subjected to 10 min of pre-treatment. The samples subjected to NH3 pre-treatment show a reduced surface-related current dispersion of 9% (compared to 16% for the untreated sample), which is attributed to the reduction of O at the SiN/epi interface. Furthermore, NH3 pre-treatment for 10 min significantly improves the current dispersion uniformity from 14.5% to 1.9%. The reduced trapping effects result in a high output power of 3.4 W mm(-1) at 3 GHz (compared to 2.6 W mm(-1) for the untreated sample). These results demonstrate that the in situ NH3 pre-treatment before LPCVD of SiN passivation is critical and can effectively improves the large-signal microwave performance of GaN HEMTs.

Structural defects in Mg-doped GaN were analyzed using high-resolution scanning transmission electron microscopy combined with electron energy loss spectroscopy. The defects, in the shape of inverted pyramids, appear at high concentrations of incorporated Mg, which also lead to a reduction in free-hole concentration in Mg doped GaN. Detailed analysis pinpoints the arrangement of atoms in and around the defects and verify the presence of a well-defined layer of Mg at all facets, including the inclined facets. Our observations have resulted in a model of the pyramid-shaped defect, including structural displacements and compositional replacements, which is verified by image simulations. Finally, the total concentration of Mg atoms bound to these defects were evaluated, enabling a correlation between inactive and defect-bound dopants.

The hot-wall metal-organic chemical vapor deposition (MOCVD), previously shown to enable superior III-nitride material quality and high performance devices, has been explored for Mg doping of GaN. We have investigated the Mg incorporation in a wide doping range ( 2.45 x 10( 18) cm(-3) up to 1.10 x 10(20) cm(-3)) and demonstrate GaN:Mg with low background impurity concentrations under optimized growth conditions. Dopant and impurity levels are discussed in view of Ga supersaturation, which provides a unified concept to explain the complexity of growth conditions impact on Mg acceptor incorporation and compensation. The results are analyzed in relation to the extended defects, revealed by scanning transmission electron microscopy, x-ray diffraction, and surface morphology, and in correlation with the electrical properties obtained by Hall effect and capacitance-voltage (C-V) measurements. This allows to establish a comprehensive picture of GaN:Mg growth by hot-wall MOCVD providing guidance for growth parameters optimization depending on the targeted application. We show that substantially lower H concentration as compared to Mg acceptors can be achieved in GaN:Mg without any in situ or post-growth annealing resulting in p-type conductivity in as-grown material. State-of-the-art p-GaN layers with a low resistivity and a high free-hole density (0.77 omega cm and 8.4 x 10( 17) cm(-3), respectively) are obtained after post-growth annealing demonstrating the viability of hot-wall MOCVD for growth of power electronic device structures. (C)2022 Author(s).