Iodine-rich inorganic perovskites possessing desirable bandgaps as well as high thermal and chemical stability are facing serious issues of low polymorphic stability, whereas chlorine-rich inorganic perovskites hold outstanding thermodynamic stability but suffer from low efficiency. Here, we develop function-gradient inorganic perovskites adopting a surface halide substitution strategy, where a stable chlorine-rich skin protects efficient iodine-rich layers, incorporating high stability of chlorine-rich perovskites with high efficiency of iodine-rich perovskites. This strategy simultaneously passivates surface defects and stabilizes the photoactive polymorphs of perovskite, leading to a power conversion efficiency of 21.2% for unit cells (0.16 cm2) and 19.2% for solar modules (23.9 cm2). Notably, the compositional gradient mitigates light-induced ion migration and enhances resistance to environmental erosion. Thus, our devices exhibit negligible efficiency loss after 1000 h storage in air and 3200 h operation under continuous 1-sun illumination at 40 degrees C, representing the most stable wide-bandgap perovskite solar cells reported to date.