CaMnO3 is a perovskite with attractive magnetic and thermoelectric properties. CaMnO3 films are usually grown by pulsed laser deposition or radio frequency magnetron sputtering from ceramic targets. Herein, epitaxial growth of CaMnO3-y (002) films on a (112 over bar 0)-oriented LaAlO3 substrate using pulsed direct current reactive magnetron sputtering is demonstrated, which is more suitable for industrial scale depositions. The CaMnO3-y shows growth with a small in-plane tilt of <approximate to 0.2 degrees toward the (200) plane of CaMnO3-y and the (1 over bar 104) with respect to the LaAlO3 (112 over bar 0) substrate. X-ray photoelectron spectroscopy of the electronic core levels shows an oxygen deficiency described by CaMnO2.58 that yields a lower Seebeck coefficient and a higher electrical resistivity when compared to stoichiometric CaMnO3. The LaAlO3 (112 over bar 0) substrate promotes tensile-strained growth of single crystals. Scanning transmission electron microscopy and electron energy loss spectroscopy reveal antiphase boundaries composed of Ca on Mn sites along and , forming stacking faults.