Commercial yarns can be functionalized with conducting polymers (CPs) todevelop yarn and textile actuators. Here we show a method of functionalizationof commercial polyamide yarns by poly-3,4-ethylenedioxythiophene:polystyrenesulfonate (PEDOT:PSS) coating. Aftercoating, while PEDOT:PSS is drying, it is possible to twist and coil the yarns,resulting in a major improvement of their linear strain and speed of movement.By using a potential window between +0.6 V and -1.2 V vs Ag/AgCl it waspossible to obtain a fully reversible actuation of a coiled yarn providing up to1.62% strain. A strain higher than 1% was achieved in less than 1 second.Compared to the untwisted, regular yarns, the twisted and coiled yarns produce>9× and >20× higher strain, respectively. These results are a step forward towardsthe development of soft, silent and compliant smart textile exoskeletons.